Product Description and Application 产品描述和用途
125℃/150℃Irradiation cross-linkable flame-retardant automotive cable compounds which are produced with mixing, plasticizing and pelletizing process, regards polyolefin resin as the basic raw material, adds flame-retardant, antioxidant and sensabilizer. The highest working temperature are respectively 125℃and 150℃. The cables with it can meet JASO D 611 Standard. These products are suitable for extruding insulation layers of JASO Standard car cables.
125℃/150℃辐照交联阻燃汽车线料以聚烯烃树脂为主要原料，加入阻燃剂，抗氧剂，助交联剂，经混炼、塑化、造粒而得，最高工作温度分别为125℃和150℃。制成电线后可以满足JASO D 611标准，适用于日标汽车线挤出绝缘层。
Processing Indicator 加工工艺：
General PVC or PE extruder is possible for the production of it. Recommend screw extruder with L/D≥25. It is better to put one 80 mesh filter on the position of screen while extruding. Temperatrue range changes according to different conditions of extruding equipment. Below temperature is just for boot debugging.
本产品可采用普通PVC或PE挤出机进行生产，建议螺杆长径比L/D≥25，挤出过程中可在网板放置一层80目滤网。下列各温度可作为开机调试的参考：
| Size规格 |
Z1 |
Z2 |
Z3 |
Z4 |
H1 |
H2 |
H3 |
H4 |
| 0.35~0.75 |
165 |
175 |
185 |
185 |
190 |
190 |
190 |
190 |
| ≥1.0 |
165 |
170 |
175 |
180 |
180 |
180 |
180 |
180 |
Conductor preheated to 110 ℃, and warm bath temperature about 40～60℃
导体预热至110℃，温水槽温度40～60℃左右。
Irradiation Process辐照工艺
Irradiation dose of irradiation cross-linkable polyolefin automotive cables compound should be given according to thermal strength requirements (note: different accelerators with the same irradiation dose will cause different thermal strength values). The thermal strength shoul be controlled between 25%-40%. Generally speaking, the more bigger conductor, the larger irradiation dose amount.
辐照交联型聚烯烃汽车线的辐照剂量应根据应以热延伸达到要求为准（不同单位加速器按同一辐照剂量，其热延伸值不一样），本产品热延伸需控制在20%～40%范围内，导体越大，辐照剂量应适当的提高。
Attentions 注意事项：
1）The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用，材料一经开封，建议12小时之内用完。
2）Please ensure the screw, barrel , hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前确保螺杆、机筒、加料斗彻底清理干净，加工过程中严禁带入杂质。
3）If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速挤出时，请慢慢逐渐加快螺杆转速，以免塑化不良，电缆表面毛糙。
Physical and Electrical Properties 物理和电气性能
Item
试验项目 |
Unit
单位 |
FEJZ125D |
FEJZ150D |
| Tensile Strength 拉伸强度 |
MPa |
≥12.5 |
≥12.5 |
| Elongation at Break 断裂伸长率 |
% |
≥250 |
≥250 |
| Density 密度 |
g/cm3 |
≤1.35 |
≤1.35 |
Dielectric Strength
介电强度 |
MV/m |
≥20 |
≥20 |
Thermal Aging Condition
热老化条件 |
/ |
150℃×240h |
180℃×240h |
Tensile strength after aging
老化后拉伸强度 |
MPa |
≥12.5 |
≥12.5 |
Tensile Strength Variation after Aging
老化后拉伸强度变化率 |
% |
±20 |
±20 |
Elongation After Aging
老化后断裂伸长率 |
% |
≥250 |
≥250 |
Elongation Variation after Aging
老化后断裂伸长率变化率 |
% |
±20 |
±20 |
Brittle Temperature with Impact
冲击脆化温度 |
℃ |
-40 |
-40 |
20℃Volume Resistivity
20℃体积电阻率 |
Ω m |
≥1.0×1012 |
≥1.0×1012 |
Hot Set Test Condition
热延伸试验条件
200℃×0.2MPa×15min |
Hot Elongation
负荷下伸长率 |
% |
≤100 |
≤100 |
Permanent Deformation after Cooling
冷却后永久形变 |
% |
≤5 |
≤5 |
Oxygen Index
氧指数 |
% |
≥22 |
≥22 |
Note: tensile speed 100mm/min or 50mm/min 注： 拉伸速度100mm/min或者50mm/min