125℃热塑性阻燃汽车线料(含卤) TEJZ125D
125 ℃ Thermoplastic Halogenous Flame-retardant Automotive Cable Compound ...
型号:0

参考价:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Product Description and Application 产品描述和用途
125 ℃thermoplastic halogenous flame-rerardant automotive cable compound is produced with mixing, plasticizing and pelletizing processes, which regards PP resin as the main basic raw materials, adds flame retardant, anti-oxidant and other additives. The highest working temperature is 125℃. Its cables can meet ISO6722 Standard. This compound is suitable for the insulation layers of 0.2 square meters and above of automotive cables.
125℃热塑性阻燃汽车线料是以聚丙烯为主要基材,加入阻燃剂,抗氧剂等助剂,经混炼、塑化、造粒而得,最高工作温度为125℃。制成电线后可以满足ISO6722标准,适用于0.2平方以上汽车线挤出绝缘层。
 
Processing Indicator 加工工艺
General PVC or PE extruder is possible for the production of it. Recommend screw extruder with L/D≥25. It is better to put one 80 mesh filter on the position of screen while extruding. Temperatrue range changes according to different conditions of extruding equipment. Below temperature is just for boot debugging.
本产品可采用普通PVC或PE挤出机进行生产,建议螺杆长径比L/D≥25,挤出过程中可在网板放置一层80目滤网。温度的选择应根据所用挤塑机的具体情况选定。下列各温度可作为开机调试的参考:
Size
规格 
Z1 Z2 Z3 Z4 H1 H2 H3 H4
0.2~0.75 185 195 205 205 220 220 220 215
≥1.0 185 190 195 210 210 215 215 215
 
Conductor preheated to 110 ℃, and warm bath temperature about 40~60℃
导体预热至110℃,温水槽温度40~60℃左右。
 
Attentions 注意事项:
1)The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用,材料一经开封,建议12小时之内用完。
2)Please ensure the screw, barrel , hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前确保螺杆、机筒、加料斗彻底清理干净,加工过程中严禁带入杂质。
3)If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速挤出时,请慢慢逐渐加快螺杆转速,以免塑化不良,电缆表面毛糙。
 
 
  Physical and Electrical Properties 物理和电气性能
Item
试验项目
Unit
单位
TEJZ125D
Tensile Strength
拉伸强度
MPa ≥13.5
Elongation at Break
断裂伸长率
% ≥250
Density
密度
g/cm3 ≤1.35
Dielectric Strength
介电强度
MV/m ≥20
Thermal Aging Condition
热老化条件
/ 150℃×240h
Tensile Strength After Aging
老化后拉伸强度
MPa ≥12.5
Tensile Strength Variation after Aging
老化后拉伸强度变化率
% ±20
Elongation After Aging
老化后断裂伸长率
% ≥250
Elongation Variation after Aging
老化后断裂伸长率变化率
% ±20
Brittle Temperature with Impact
冲击脆化温度
-40
20℃Volume Resistivity
20℃体积电阻率
Ωm ≥1.0×1012
Oxygen Index
氧指数
% ≥24
Hardness
硬度
ShoreD ≤55
 
Note: tensile speed: 50mm/min
注: 拉伸速度50mm/min