辐照交联阻燃绝缘料 FEJZ105, FEJZ125, FEJZ150
Irradiation Cross-linkable Flame Retardant Insulation Compound...
型号:0

参考价:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Product Description and Application 产品描和用途
This product is a kind of insulation compounds, which can be irradiated and cross-linked. It doesn’t contain heavy metals like Pb, Ba, Cd, Sn and Sb. It can meet ROHS Standard and its cables can pass VW-1 burning requirements. The highest working temperature is 150℃, and is mainly used for various control cables, instrument wires of automotive low-voltage wires, installment wires and electric wires.
该材料是一种可以辐照交联的阻燃绝缘料,不含Pb、Ba、Cd、Cr、Sn、Sb六大重金属, 满足RoHS标准要求,电线能满足VW-1的燃烧要求,最高工作温度150℃。主要用于各类控制电缆,汽车低压电线电缆的仪器仪表, 安装电线电缆,电子线。
 
Processing Indicator 加工工艺
Recommend to use single ordinary screw extruder with L/D=20-25.
建议使用普通单螺杆挤出机进行加工,长径比L/D=20-25。
Model
牌号
Machine Barrel Temperature
机筒温度
Molding Temperature
机头温度
FEJZ105/FEJZ125/FEJZ150 130-140℃ 150-160℃
 
 
 
 
 
Physical and Electrical Properties 物理及电性能指标
Item
试验项目
Unit
单位
Technical requirements
技术要求
FEJZ105 FEJZ125 FEJZ150
Tensile Strength
拉伸强度
MPa ≥12.5(8.0) ≥12.5(8.0) ≥12.5(8.0)
Elongation at Break
断裂伸长率
% ≥250 ≥250 ≥250
Density
密度
g/cm3 ≤1.35 ≤1.35 ≤1.35
Dielectric Strength
介电强度
MV/m ≥20 ≥20 ≥20
Aging Condition
热老化条件
/ 136℃×168h 158℃×168h 180℃×168h
Variation of Tensile Strength After Aging
老化后拉伸强度变化率
% ±20 ±20 ±20
Elongation Variation After Aging
老化后断裂伸长率变化率
% ±20 ±20 ±20
Brittle Temperature With Low Temperature Impact
低温冲击脆化温度
≤-40 ≤-40 ≤-40
20℃Volume Resistivity
20℃体积电阻率
/ ≥1.0×1012 ≥1.0×1012 ≥1.0×1012
Hot Set Test Condition热延伸试验条件
200℃×0.2MPa×15min
Hot Elongation
负荷下伸长率
% ≤80 ≤80 ≤80
Permanent Deformation after Cooling
冷却后永久形变
% ≤5 ≤5 ≤5
Oxygen Index
氧指数
% 28 28 28
Burning Level
燃烧等级
/ 94-v-0 94-v-0 94-v-0
 
1、The recommended dose of irradiation pull :12 -18 megabytes. 建议的辐照剂量为:12-18兆拉。
2、The data in()is measured before irradiation.           ()中的数据为,辐照之前的数据。