辐照交联聚烯烃绝缘料 FEJ90, FEJ105, FEJ125, FEJ150
Irradiation Cross-linkable Polyolefin Insulation Material...
型号:0

参考价:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Product description 产品描述
FEJ90, FEJ105, FEJ125 and FEJ150 are irradiation cross-linkable insulation compounds for wire and cables, which regards polyolefin resin as the basic raw material, and adds anti-oxidant, cross-linkable agent and modified agents and other additives. They have excellent extruding property and physical property and can be widely used for various control cables, instrument installment wires of automotive low-voltage wires, and electrical wires. The highest working temperature is 90-150℃. Moreover, they don’t contain heavy mentals like Pb, Ba, Cd, Cr, Sn and Sb, and all their properties can meet the requirements of ROHS Standard.
FEJ90、FEJ105、FEJ125和FEJ150是以聚烯烃树脂为基料,添加抗氧剂、交联剂、改性剂等各种助剂的可辐照交联绝缘电缆料。它兼有良好的挤出性能和物理性能,可广泛用于各类控制电缆,汽车低压电线电缆的仪器仪表安装电线电缆,电子线,最高工作温度为90-150℃。另外它不含有如Pb、Ba、Cd、Cr、Sn、Sb的重金属,且所有性能都能很好的满足ROHS标准要求。
 
Processing Indicator 加工工艺
Recommend to use single ordinary screw extruder with L/D=20-25.
建议使用普通单螺杆挤出机进行加工,长径比L/D=20-25。
Model
牌号
Machine Barrel Temperature
机筒温度
Molding Temprature
机头温度
FEJ90/FEJ105/FEJ125/FEJ150 165℃-185℃ 185℃-195℃
 
 
Physical and Electrical Properties 物理及电性能指
Item
试验项目
Unit
单位
Technical requirements
技术要求
FEJ90 FEJ105 FEJ125 FEJ150
Tensile Strength
拉伸强度
Mpa ≥13.5 ≥13.5 ≥13.5 ≥13.5
Elongation at Break
断裂伸长率
% ≥350 ≥350 ≥350 ≥350
Density
密度
g/cm3 <1 <1 <1 <1
Dielectric Strength
介电强度
MV/m ≥25 ≥25 ≥25 ≥25
Aging Condition
热老化条件
/ 121℃
×168h
136℃
×168h
158℃
×168h
180℃
×168h
Tensile Strength Variation After Aging
拉伸强度变化率
% ±20 ±20 ±20 ±20
Elongation Variation After Aging
断裂伸长率变化率
% ±20 ±20 ±20 ±20
Brittle Temperature With Low Temperature Impact
低温冲击脆化温度
≤-76 ≤-76 ≤-76 ≤-76
20℃Volume Resistivity
20℃体积电阻率
Ω.cm ≥1×1013 ≥1×1013 ≥1×1013 ≥1×1013
Hot Set Test Condition
热延伸试验条件
200℃×0.2MPa×15min
Hot Elongation
负荷下
伸长率
% ≤80 ≤80 ≤80 ≤80
Permanent Deformation after Cooling
冷却后永久形变
% ≤5 ≤5 ≤5 ≤5
 
Recommend irradiation dose:12 -18 megabytes. 建议的辐照剂量为:12-18兆拉。